RC PF 42 SERIES
Properties
Good flexibility, opacity and heat formability.
PC, Rigid PVC, Treated PET. Especially for industrial applications.
INTRODUCTIONS
RC PF 42 SERIES forms flexible ink film with matt finish. RC PF is suitable for polycarbonate industrial meters which require post-print processing. RC PF is also recommendable for membrane switches of treated PET films.
APPLICATIONS
Polycarbonate, treated PET films, PVC stickers, rigid vinyl, AS, ABS, acryl(injections), paper
CHARACTERISTICS
1. Flat and matt finish. Excellent flexibility.
2. High density and high opacity.
3. Adhesion and over-printability are good.
4. Reproducibility of fine patterns is good.
5. Stable on the screen.
HOW TO USE
1. Ink is supplied in ready-to-use condition. Stir well before use. Matt finish can be obtained after UV curing.
2. Add 42-00 REDUCER up to 10% to lower viscosity. Viscosity is lowered without spoiling matt finish.
3. The grade of matt finish changes depending on curing conditions or environmental temperature although it does not change after curing. To up-grade matt finish, take more time for levelling.
4. Standard curing conditions(The conditions depend on the substrates.)
One metal halide lamp 120 W/cm, Distance from focus : 10 cm
Conveyor speed : 5 m/min (Integral light : approx. 500 mJ/cm²)
5. Mesh : 300-350 meshes/inch, Thickness of sol : <10 microns
COVERAGE
70-80 m²/kg
TYPE OF PACKING
1 kg PLASTIC CONTAINER
COLOR RANGE
COLORS
OPAQUE WHITE, LEMON YELLOW, YELLOW, DEEP YELLOW,ORANGE, BRIGHT RED, RED, GERANIUM, VIOLET, DEEP BLUE, BLUE, MARINE BLUE, GREEN, BLACK
CLEAR
CLEAR, MATT CLEAR, COMPOUND
HFT MATT CLEAR : Flat and matt
UB-1 MATT CLEAR : Fine textured surface (high density)
MATT CLEAR : Fine textured surface (low density)
PRECAUTIONS
1. Skin irritation(P.I.I.) of each color is low(under 2.0). However, it is advised to avoid skin contact. In case of skin contact, please wash with soap and water immediately.
2. Store the ink in a cool and dark place. Stir occasionally to keep stability when the ink is stored for a long time.
3. Stir well before use as de-foamer might be separated.
4. Standard thickness of colored ink film is 10-12 microns. If the thickness exceeds 15 microns, insufficient curing may cause poor adhesion.
5. Please refer to MSDS before use.
6. Be sure to do trial print before commercial run to confirm that the product fits the purposes.
PHYSICAL PROPERTIES
– Substrate : Polycarbonate (thickness : 0.5 microns) HINTO(TOYOBO), HKU-31(HIGASHIYAMA FILM)
– Meshes : Polyester 350 meshes/inch, Thickness of sol 10 microns,
– Thickness of printed ink film : 10 microns
– Curing : One metal halide lamp 120 W/cm
– Conveyor speed : 5 m/min. (Integral light : 500 mJ/cm²)
| TEST ITEMS | TEST METHODS | RESULTS |
|---|---|---|
| Adhesion | Cross-hatch, tape-peeling test | 100/100, Pass |
| Hardness | JIS K-5400 8.4 Pencil hardness | B-HB |
| Flexibility | Bending test (JIS K-5400 8.1) | Excellent |
| Impact resistance | JIS K-5400 8.3 Du Pont Impact tester 1/2 inch, 500 grams, 50 cm |
Pass |
| Over-printability | Adhesion test after 3-color-overprint | 100/100 Pass |
| Heat resistance | 70°C(158°F), 240 hours | Pass |
| Humidity resistance | 60°C(140°F), 95%RH, 240 hours | Pass |
| Coldness resistance | -20°C(-4°F), 240 hours | Pass |
| Water-proofness | 40°C(104°F)-warm water, 24 hours | Pass |
| Alcohol resistance | Rubbing test with 99.5% ethanol | Gloss slightly spoiled after 50 times. |
| Weathering resistance | Sunshine weather meter-400 hours | Pass |
| Key-rubbing resistance | Repeated operation with JIS C-5307 based on JIS C-5441 |
million times : Pass on treated PET film 188 microns |
1. Weathering resistance depends on the color. Please refer to lightfastness chart before use.
2. Information given here is gained from our laboratory testing, and no firm
guarantee is implied.
Applications Usage
PC, Rigid PVC, Treated PET. Especially for industrial applications.